Structural characterization of Li2(MgxZn1-x)2W2O9 for bluish-white luminescence in rare earth-free tungstate phosphors.
Physical chemistry chemical physics : PCCP(2024)
摘要
Self-activated phosphors have attracted considerable attention due to their low synthesis temperature, high excitation threshold, and broad emission spectrum. And self-activated tungstate phosphors are distinguished by their low cost and stable chemical properties. Generally, it is difficult to observe luminescence from tungstate phosphors at room temperature. Furthermore, blue-emitting tungstate phosphors with high quantum efficiency are rarely reported. In this study, we succeeded in discovering high quantum-efficiency bluish-white-emitting Li2(MgxZn1-x)2W2O9 phosphors and investigating their detailed crystal structures. Upon near-ultraviolet excitation at 266 nm, these phosphors exhibit a broadband emission peak. The red shift of emission is slight with increasing Zn content in Li2(MgxZn1-x)2W2O9. A highly compact octahedral [WO6] unit is observed in the Li2(MgxZn1-x)2W2O9 phosphors. The phosphors exhibit high internal quantum efficiencies (IQEs) of 68.70% (M = Mg), 43.90% (M = Mg0.5Zn0.5), and 22.90% (M = Zn), respectively. This study provides a bluish-white-emitting tungstate phosphor with high quantum efficiency.
更多查看译文
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要