Cleanliness Improvement and Microstructure Refinement of As-Cast High-Nitrogen Stainless Bearing Steel by Magnesium Treatment
Metallurgical and Materials Transactions B(2024)
Abstract
The influence of magnesium treatment on cleanliness and microstructure characteristics of as-cast high-nitrogen stainless bearing steel (HNSBS) was systematically investigated. Results manifested that as the magnesium content increased from 0.0003 to 0.0054 wt pct, the oxygen and sulfur contents in steel, along with the number density and average size of inclusions significantly decreased due to the strong thermodynamic affinity and the removal of inclusions. Meanwhile, the inclusion evolution processes were Al2O3 → MgO·Al2O3 → MgO and MnS → MgS + Mg3N2, and the magnesium content in HNSBS should not exceed 0.0047 wt pct to prevent the formation of deleterious Mg3N2 inclusion. Additionally, the secondary dendrite spacing and the area fraction of precipitates (M23(C, N)6 and M2(C, N)) at the 1/2 radius of ingots decreased form 83 ± 25 μm and 17 pct to 63 ± 16 μm and 12 pct, respectively. The dendrite structure was refined owing to the increase in effective nucleation sites for γ-Fe provided by MgO·Al2O3 and MgS inclusions, as well as the enrichment of magnesium in the liquid phase at solidifying front. The area fraction and size of precipitates were reduced due to the decrease of chromium activity. The finer and more dispersed precipitates was attributed to the reduction of growth space and increase in effective nucleation sites. This work provides theoretical guidance for preventing the formation of deleterious inclusions (especially for nitrides) in high-nitrogen alloy systems and refining the microstructure of alloy systems containing M23(C, N)6 and M2(C, N) precipitates.
MoreTranslated text
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined