Anti-ageing and rheological performance of bitumen modified with polyaniline nanofibres

Asphalt pavements represent the great majority of roads worldwide. However, the bitumen physico-chemical properties change due to ageing processes during both the production and service life of the asphalt mixes. In recent years, a completely new trend has been observed in the road engineering industry oriented to extending the service life of roads, bringing direct economic, ecological and social benefits. This work presents the possibility of inhibiting ageing of road bitumen by using polyaniline nanofibers (PANI_NFs) as well as enhancing its rheological properties examined with Linear Amplitude Sweep (LAS) as well as Multiple Stress Creep and Recovery (MSCR) tests. These results show that the application of PANI_NFs maintains the primary penetration value of bitumen short-term and long-term aged road bitumen at 88 % and 52 %, respectively. Moreover, bitumen modification with PANI_NFs reduces the softening temperature increase by 33 % and 24 %, respectively, and the viscosity increase of road asphalt by 50 % and 25 %, respectively. PANI_NFs also stabilised the bitumen surface adhesion force, determined with AFM, consequently confirming the enhanced resistance to ageing processes. In addition, changes in the carbonyl index, sulphoxide index and aromaticity of bitumen demonstrated that PANI_NFs inhibit oxidation and aromatisation reactions of its components. The tests indicated a 4-fold decrease in the degree of bitumen component oxidation after short-term ageing and a 33 % decrease after long-term ageing. FTIR analysis also showed a reduction in the degree of bitumen component aromatisation process of 79 % and 76 % for short-term and long-term ageing, respectively. The LAS and MSCR test results also showed that PANI_NFs had a beneficial impact on the resistance of the bitumen to fatigue and rutting. Overall, the study results suggest that PANI_NFs consitute a promising modifier for bitumen in terms of ageing inhibition and performance characteristics.