Advanced quasi-solid-state lithium-sulfur batteries: A high-performance flexible LiTa2PO8-based hybrid solid electrolyte membrane with enhanced safety and efficiency
JOURNAL OF ENERGY STORAGE(2024)
Abstract
Quasi-solid-state lithium-sulfur battery (QSSLSB) systems are more reliable and effective when considering safety and performance. This study employs a solution-casting method to create a self-supporting hybrid solid-state electrolyte (HSE) membrane. The membrane comprises a novel interconnected fast Li-ion conducting oxide, LiTa2PO8 (LTPO, filler); poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP, polymer matrix); lithium bis (trifluoromethanesulfonic) imide (LiTFSI, salt); and succinonitrile (SN, plasticizer). The as-prepared LTPO-HSE composite membrane was assembled with a sulfurized polyacrylonitrile (SPAN) cathode and Li anode. The composite membrane exhibited good compatibility with the cathode, decreased the interfacial resistance, and delivered a higher Li+ ion transport number (ca. t(Li)(+) = 0.78). According to galvanostatic intermittent titration technique GITT test results, the 2032-type LiS cells with LTPO-HSE membranes have an average Li+ ion diffusion coefficient of about 1.06 x 10(-10) cm(2) s(-1). Furthermore, the symmetrical cells that have Li metal and LTPO-HSE membrane exhibit smoother Li plating/stripping for 100 h at a current density of 1 mA cm(-2). At 0.2C, the SPAN/LTPO-HSE/Li full cell exhibits a high initial capacity of 1189 mAh g(-1), after 200 cycles, it maintained a specific capacity of 1118 mAh g(-1) with a steady Coulombic efficiency of 99.9 %. At a decay rate of 0.02 % per cycle, the capacity retention is 96 % (from the second cycle onward). Furthermore, our QSSLSB cell exhibits better capacity retention of 81 % after 350 cycles at 0.5C. In-situ microcalorimetry (MMC) revealed that the total exothermic heat generation (Q(t)) in coin cells based on quasi-solid LTPO-HSE membrane, cycling at 5C and 35 degrees C, was significantly lower (similar to 60.2 % during discharge and 66.8 % during charge) that generated by the cells that use glass fiber separator with liquid-electrolyte GF-LE systems. Owing to its flexibility, better transference number, wider electrochemical window, and minimal heat generation, the as-prepared single-layer LTPO-HSE membrane is a promising solid-state electrolyte for future solid-state lithium-sulfur battery applications.
MoreTranslated text
Key words
Quasi-solid-state lithium-sulfur batteries (QSSLSB),Sulfurized polyacrylonitrile (SPAN),Poly(vinylidene fluoride- co- hexafluoropropylene) (PVDF-HFP),Hybrid solid electrolytes (HSE),LiTa (2) PO (8) (LTPO),Reduced heat generation
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined