Degradation of Pollutants and Photocatalytic H2 Evolution Using Carbon Nanotube/Ag Nanoparticle-Modified BaTiO3 Nanoparticles
ACS Applied Nano Materials(2024)
摘要
A ternary nanocomposite, BaTiO3-CNT/Ag, was synthesized via a coprecipitation method to function as a photocatalyst for pollutant degradation and H-2 production through a water-splitting reaction. The successful preparation of the nanocomposite and the enhancement of its morphological properties were confirmed through Raman spectroscopy, X-ray diffraction/photoelectron spectroscopy (XRD/XPS), and scanning/transmission electron microscopy (SEM/TEM) studies. Utilizing transient photocurrent, photoluminescence (PL) spectroscopy, UV-visible diffuse reflectance spectroscopy (DRS), Mott-Schottky, and electrochemical impedance spectroscopy (EIS) tests, it was determined that the incorporation of carbon nanotube (CNT) and Ag into BaTiO3 led to a promotion of charge separation efficiency up to 15 times, a decrease in the bandgap energy from 3.12 to 2.85 eV, larger band bending, lower electron/hole recombination, and extensive lower internal resistance. In photodegradation-related studies, the response surface methodology (RSM) method was performed for experimental design to optimize the amounts of photocatalyst dosage, irradiation time, and initial dye concentration, yielding optimal values of 0.681 g/L, 67.5 min, and 1 mg/L, respectively. The sample showed outstanding photocatalytic efficiency in the degradation of different organic water pollutants, coupled with remarkable stability and reusability, as evidenced by a four-run cyclic experiment. Finally, the evaluation of H-2 production revealed a remarkable amount of 542.4 mu mol/gh for the ternary nanocomposite, which is about 5 times higher than that of the pure BaTiO3 sample. This research provides thorough insight into the synthesis of a ternary nanocomposite that extremely enhances the charge transfer abilities and, therefore, boosts the photocatalytic H-2 production and photodegradation of pollutants.
更多查看译文
关键词
BaTiO3,CNT,plasmonic,photocatalysis,water splitting,response surfacemethodology
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要