Dystrophic calcinosis: structural and morphological composition, and evaluation of ethylenediaminetetraacetic acid (‘EDTA’) for potential local treatment

To perform a detailed morphological analysis of the inorganic portion of two different clinical presentations of calcium-based deposits retrieved from subjects with SSc and identify a chemical dissolution of these deposits suitable for clinical use. Chemical analysis using Fourier Transform IR spectroscopy (‘FTIR’), Raman microscopy, Powder X-Ray Diffraction (‘PXRD’), and Transmission Electron Microscopy (‘TEM’) was undertaken of two distinct types of calcinosis deposits: paste and stone. Calcinosis sample titration with ethylenediaminetetraacetic acid (‘EDTA’) assessed the concentration at which the EDTA dissolved the calcinosis deposits in vitro. FTIR spectra of the samples displayed peaks characteristic of hydroxyapatite, where signals attributable to the phosphate and carbonate ions were all identified. Polymorph characterization using Raman spectra were identical to a hydroxyapatite reference while the PXRD and electron diffraction patterns conclusively identified the mineral present as hydroxyapatite. TEM analysis showed differences of morphology between the samples. Rounded particles from stone samples were up to a few micron in size, while needle-like crystals from paste samples reached up to 0.5 µm in length. Calcium phosphate deposits were effectively dissolved with 3