Y2GaSbO7: A novel microwave dielectric ceramic with pyrochlore structure
JOURNAL OF ALLOYS AND COMPOUNDS(2024)
摘要
Ceramics of Y2GaSbO7 (YGSO) were prepared by the solid-state reaction method. The ceramics were confirmed by XRD and TEM to exhibit the Fd-3 m (227) space group and a cubic pyrochlore structure within the temperature range of 1420-1500 C. XPS verified that the valence states of Y, Ga, and Sb in the ceramics were + 3, + 3, and + 5, respectively. Additionally, the relationship between the FWHM of the notable peak at 775 cm- 1 and the Q x f value was elucidated through Raman spectroscopic analysis. The analysis of the P-V-L theory revealed that the Sb-O bond is crucial in determining er, while the values of rf and Q x f are affected by the Y-O bond. At 1460 C, YGSO ceramics obtained the maximum relative density (97.5%) and the best microwave dielectric properties (er = 14.78, Q x f = 50,153 GHz, and rf = -22.3 ppm/C).
更多查看译文
关键词
Pyrochlore structure,Microwave dielectric properties,P-V-L theory,Y2GaSbO7
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要