Contrasting Irradiation Behavior of Dual Phases in Ti-6Al-4V Alloy at Low-Temperature Due to ω-phase Precursors in β-phase Matrix

Aiming to simulate the radiation damage effect on a dual α+β phase Ti-6Al-4V alloy utilized as high-intensity accelerator beam window material, a series of irradiation experiments were conducted with a 2.8 MeV-Fe2+ ion beam in several dpa regions at room temperature. The nano-indentation hardness increased steeply at 1dpa and unchanged up to 10dpa, due to the saturation of defect clusters and tangled dislocations in the dominant α-phase matrix with a size of 2~3nm and a density of about 1×1023m-3. In contrast in the intergranular β-phase, larger loops of 20~30nm diameter were observed with much less density of about 5×1020m-3. The diffraction pattern showed rectilinear diffuse streaks between the β-phase reflections, corresponding to the ω-phase precursor, without dose dependency in its intensity. FFT/I-FFT analysis of the HREM revealed a sub-nanometer-sized lattice disorder with local fluctuations, not discrete but continuous, and homogeneously distributed within the matrix β-phase stably against the irradiation. The significantly low dislocation density and the absence of phase transformation in the β-phase matrix could be attributed either to the strong sink effect expected for this distinctive sub-nanometer-sized homogeneous lattice disorder or to the anomalous point defect recombination induced by the high mobility of vacancies, both of which are originated from the metastable ω-phase precursors specifically formed in the β(BCC) phase of group-4 transition metals.