Improved electrical transport properties of La0.7Ca0.3−xKxMnO3 (0.0 ≤ x ≤ 0.3) films grown on La0.3Sr0.7Al0.65Ta0.35O3 (00l) substrates by sol–gel spin coating method
Ceramics International(2024)
摘要
Herein, La0.7Ca0.3−xKxMnO3 (LCKMO) films with highly oriented growth were prepared on La0.3Sr0.7Al0.65Ta0.35O3 (00l) substrates by sol–gel spin coating method. Comprehensive analysis of microstructure, surface morphology, ion valence, and electrical transport properties of LCKMO films indicates that the substitution of K+ ions for Ca2+ ions increased the ratio of Mn4+/(Mn3+ + Mn4+), narrowed single electron bandwidth, and enhanced double exchange mechanism and electron–lattice coupling. Moreover, the doping of K+ ions induced the dense and uniform conical-structured growth of grains on the surface of the films. Results demonstrated that at x = 0.1, LCKMO film exhibited the maximum TCR of 17.84% K−1 at 253.07 K, which was 31.76% higher than that of previously reported La1−x−yCaxKyMnO3 ceramic with the highest TCR. Further theoretical insights into the effects of Ca/K co-doping on electrical transport properties were supplemented.
更多查看译文
关键词
La0.7Ca0.3−xKxMnO3 films,Sol–gel spin coating method,Temperature coefficient of resistivity (TCR)
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要