Irradiation Effects on Tensile Properties of Reduced Activation Ferritic/Martensitic Steel: A Micromechanical-Damage-Model-Based Numerical Investigation

The tensile properties of reduced activation ferritic/martensitic (RAFM) steels are significantly influenced by neutron irradiation. Here, a mechanism-based model taking account of the typical ductile damage process of void nucleation, growth, and coalescence was used to study the temperature and irradiation effects. The elastic–plastic response of RAFM steels irradiated up to 20 dpa was investigated by applying the GTN model coupled with different work hardening models. Through a numerical study of tensile curves, the GTN parameters were identified reasonably and satisfying simulation results were obtained. A combination of Swift law and Voce law was used to define the flow behavior of irradiated RAFM steels. The deformation localization could be adjusted effectively via setting the nucleation parameter εn close to the strain where necking occurs. Because εn changed with uniform elongation, εn decreased with the testing temperature and rose with an irradiation temperature above 300 °C. The nucleation parameter fn increased with the testing temperature for RAFM steels before irradiation. For irradiated RAFM steels, fn barely changed when the irradiation temperature was below 300 °C and then it rose at a higher irradiation temperature. Meanwhile, the ultimate strength of the simulated and experimental curves showed good agreement, indicating that this method can be applied to engineering design.