Preparation and Corrosion Resistance of Superhydrophobic Coatings on 7005 Aluminum Alloy

Huilan Huang, Feng Guo, Xintao Li, Peng Xia, Li Yang, Chuanbo Hu

COATINGS(2024)

引用 0|浏览2
暂无评分
摘要
Composite coatings on the surface of a semi-continuous cast 7005 aluminum alloy under different aging treatments (T6, RRA, and FSA) are presented and characterized in this research. SiO2 combined with stearic acid (STA) modified by KH550 was utilized to achieve multifunctional superhydrophobic coatings. Adhesive tape adhesion, blade scratch, and mechanical wear tests were utilized to assess the durability of the superhydrophobic coatings. The results showed that the prepared coatings exhibited excellent superhydrophobicity, self-cleaning ability, and mechanical properties, especially the T6 temper alloy. This alloy had the largest CA value (156.5 degrees) and the lowest SA value (4.3 degrees). The composite coatings still exhibited excellent superhydrophobicity under mechanical damage. Furthermore, the alloys with STA/SiO2 displayed marvelous corrosion resistance efficiency. The T6 temper alloy with a protection rate of 73.8% had an approximately one-order-of-magnitude decrement in carrion current density. The composite coating can be effectively utilized in various industrial fields, thus extending its potential impact.
更多
查看译文
关键词
7005 aluminum alloy,multistage aging treatment,superhydrophobic,sol-gel
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要