Elastic properties and microstructure evolution of Zn2SnO4-spinel-containing composite ceramics based on tin oxide and zinc oxide
Journal of the European Ceramic Society(2024)
摘要
Ceramics based on tin oxide (SnO2) and zinc oxide (ZnO) were sintered at temperatures up to 1400 °C. Except for the end members, all these ceramics are two- or three-phase composites containing spinel phase (Zn2SnO4). Similar to pure SnO2 ceramics, also the spinel-rich composite (50:50 mixture) does not exhibit densification after sintering at 1400 °C. Spinel Zn2SnO4 is formed in all composites, with a major increase of spinel content at around 1000 °C. Young’s modulus values, determined via impulse excitation, are between the exponential relation for convex pores and a benchmark relation for concave pores (or a percolation relation). The evolution of Young’s modulus during sintering reveals significant differences between SnO2 (weak increase above 1000 °C), ZnO (significant increase above 800 °C) and the composites (intermediate). Spinel formation is revealed during heating by a distinct peak (elastic anomaly) at around 1000 °C.
更多查看译文
关键词
tin oxide,zinc oxide,tin-zinc-spinel (Zn2SnO4),elastic properties,microstructure
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要