Grain boundary, electrical transport and thermoelectric properties of the ultra-high rGO amount of C12A7-rGO composites

The Ca12Al14O33 ceramic (C12A7) and reduced graphene oxide (rGO) composite which an ultra-high amount (i.e., 40, 50, 60, and 70 wt%) of rGO (ultra-high amount C12A7/rGO composite) were synthesized by a solid-state reaction process. After the hydraulic press, the heat treatment in the temperature range of 773 K under the argon environment had been performed with the composite pellets for 30 min. XRD results of the C12A7 and all the ultra-high amount C12A7/rGO composites indicated a pure phase of C12A7 ceramic. Raman spectra confirmed the existence of rGO content in all the ultra-high amount C12A7/rGO composites. Raman peaks also suggested reduction of the free and ions from the framework of the ultra-high amount C12A7/rGO composites. SEM image presented the homogeneous grain boundary interface after the heat treatment at 773 K of the C12A7 wrapped by the rGO sheet, the agglomerated rGO sheet, and the rough interface stack of rGO sheets. UV-VIS spectroscopy presented the absorption behavior, direct energy gap, and indirect energy gap modifications of the ultra-high amount C12A7/rGO composites. Electrical conductivity of the ultra-high amount C12A7/rGO composites illustrated larger than 108 times improvement with temperature independence. Range of -5 to -17 , temperature dependence, and increased with rGO content increasing Seebeck coefficient were reported. Thermal conductivity of the ultra-high amount C12A7/rGO composites was increased with the rGO content increasing. Both the Power factor (PF) and the figure of merit (ZT) of the ultra-high amount C12A7/rGO composites were temperature dependent and were increased with the rGO content increasing, within the range of 0.4 of PF and the range of of ZT, respectively. These experimental results verified grain boundary, modified energy band, electrical transport properties and thermoelectric properties of C12A7/rGO composites loading with ultra-high content rGO