Outstanding high-temperature microwave absorption properties of La0.9Sr0.1MnO3/Ba3.75La9.5Ti18O54 composite ceramics
Journal of Alloys and Compounds(2024)
摘要
High-temperature microwave-absorbing materials are crucial for achieving radar stealth in high-speed equipment. In response to this necessity, we investigated xLa0.9Sr0.1MnO3/(1-x)Ba3.75La9.5Ti18O54 composite ceramics under variable temperatures, where x ranges from 20-50wt%. X-ray diffraction analysis indicates the coexistence of La0.9Sr0.1MnO3 and Ba3.75La9.5Ti18O54 when x ranges from 20-30wt%, transforming into a perovskite-structured solid solution with a higher proportion of La0.9Sr0.1MnO3. Variable-temperature direct current conductivity reveals a controllable transition from dielectric behavior to semiconductor behavior, resulting in the dielectric properties of composite ceramics shifting from low-loss to high loss characteristics. For x values ranging from 20wt% to 40wt%, there consistently exists a corresponding temperature and frequency range ensuring specific absorption performance. Notably, the composite ceramic with x=30wt% and a thickness of 1.1mm demonstrates an effective absorption bandwidth (RL<-10dB) of 1.75GHz within the temperature range of 400-600℃. These findings suggest that composite ceramics comprising La0.9Sr0.1MnO3 and Ba3.75La9.5Ti18O54 hold promise as high-temperature microwave-absorbing materials.
更多查看译文
关键词
High temperature performance,microwave absorption,La0.9Sr0.1MnO3,Ba3.75La9.5Ti18O54,Oxide ceramics
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要