Unleashing the potential of nano-bainite bearing steels: Controllable selection of microstructure evolution enables concurrent improvement of toughness and hardness by pre-cold deformation

In the face of increasingly demanding service conditions for high-end bearings, the need for bearing steels that demonstrate superior mechanical properties, specifically a robust balance of strength and toughness, is growing. The adoption of near-net-shaped cold rolling methods has emerged as a leading international technology to enhance bearing performance. In this study, the effect mechanisms of pre-cold deformation on the phase transformation kinetics, microstructure evolution and mechanical properties of nano-bainite bearing steels are systematically studied. Results reveal that pre-cold deformation treatment effectively reduces the Ac1 temperature of the experimental steel, expedites nano-bainite transformation and promotes strong variant selection during bainite phase transformation. With the increase in pre-cold deformation from 0 % to 50 %, the size of the prior austenite grains decreases from 6.7 μm to 3.3 μm, and the size of carbides in specimens becomes more uniform, whilst the refinement of austenite grains can considerably reduce the thickness of bainitic ferrite plates. The decrease in grain size and the increase in V1–V2 variant pairs lead to an improvement in the toughness of the nano-bainite bearing steel from 64.9 J/cm2 to 114.3 J/cm2. A marginal increase in the hardness of the bearing steel is observed with the increase in pre-cold deformation. Furthermore, this study discusses the evolution mechanism of microstructure in the subsequent phase transformation by different microstructures in the early stage. Results show that pre-cold deformation leads to the transition of the martensite twin substructure in the specimens from {112} <111> twins to twinned variants. These insights offer critical understanding into the microstructural underpinning the enhanced performance of nano-bainite bearing steels subjected to pre-cold deformation treatment.