Formation of Grown-In Nitrogen Vacancies and Interstitials in Highly Mg-Doped Ammonothermal GaN

The formation of intrinsic point defects in the N-sublattice of semi-insulating Mg-doped GaN crystals grown by the ammonothermal method (SI AT GaN:Mg) was investigated for the first time. The grown-in defects produced by the displacement of nitrogen atoms were experimentally observed as deep traps revealed by the Laplace transform photoinduced transient spectroscopy in the compensated p-type crystals with the Mg concentrations of 6 x 10(18) and 2 x 10(19) cm(-3) and resistivities of similar to 10(11) Omega cm and similar to 10(6) Omega cm, respectively. In both kinds of materials, three closely located traps with activation energies of 430, 450, and 460 meV were revealed. The traps, whose concentrations in the stronger-doped material were found to be significantly higher, are assigned to the (3+/+) and (2+/+) transition levels of nitrogen vacancies as well as to the (2+/+) level of nitrogen split interstitials, respectively. In the material with the lower Mg concentration, a middle-gap trap with the activation energy of 1870 meV was found to be predominant. The results are confirmed and quantitatively described by temperature-dependent Hall effect measurements. The mechanism of nitrogen atom displacement due to the local strain field arising in SI AT GaN:Mg is proposed and the effect of the Mg concentration on the charge compensation is discussed.