Self-cleaning antireflected surfaces based on treated PEO/SiO₂ nanocomposite films

In this study, the polyethylene oxide (PEO)/SiO2 nanoparticles (NPs) nanocomposite films with various SiO2 NPs concentrations were prepared using an in situ formation of NPs in the polymer matrix for self-cleaning antireflected surface applications. The effect of SiO2 NPs in PEO/SiO2 NPs nanocomposite films on the structural, morphological, chemical, thermal, optical, and electrical properties of PEO/SiO2 NPs nanocomposite films was performed. According to the x-ray diffraction and the differential scanning calorimetry analysis, the crystallinity degree of the nanocomposite films decreases by increasing the SiO2 NPs concentrations. The bandgap energy of PEO/SiO2 NPs nanocomposite films decreases from 3.95 to 3.55 eV as the SiO2 NPs concentration increases up to 10 wt.%. The average electrical conductivity of the PEO/SiO2 NPs nanocomposite films increases from 5.1 x 10(-7) to 2.0 x 10(-6) S/cm as the SiO2 NPs concentration increases up to 10 wt.%. The refractive index decreases to 1.64 at 550 nm for the PEO/SiO2 NPs nanocomposite films with 10 wt.% of SiO2 NPs, and the water contact angle decreases to around 0(degrees) after thermal treatment, which confirms that the PEO/SiO2 NPs nanocomposite films can be used as self-cleaning antireflected surfaces. Morphological and particle dispersion of PEO/SiO2 nanocomposite films. image