A durable coating constructed by metal-organic framework and polyphosphazene for flame retardant cotton fabric with enhanced mechanical properties
Next Materials(2024)
Abstract
The extremely flammable cellulose macromolecules in cotton fabrics seriously affect their application in the field of flame retardancy. In this paper, the surface of cotton fabric was modified with citric acid, and then metal-organic framework (UiO-66), cationic starch (St) and polyphosphonitrile (PZS) microspheres containing the transition metal element Zr were sequentially deposited to prepare an efficient and economical cotton fabric. St-PZS double-impregnated cotton fabrics have better thermal stability, flame retardancy and mechanical properties. And the coating does not affect the whiteness and stiffness of the cotton fabric. The results of thermogravimetric analysis showed that cotton/UiO-66/2St-PZS had a higher residual char rate (25.34%) under N2 atmosphere, which was 200.1% higher than that of control cotton (8.28%). In addition, cotton/UiO-66/2St-PZS had a 46.6% reduction in peak heat release, a 31.7% reduction in total heat release, and a 35.3% reduction in the peak of CO2 production compared to control cotton. It is worth noting that the average gross calorific value is 63.3% lower than that of the control cotton, indicating that flame retardant cotton fabrics can effectively inhibit the production of flammable gases. In addition, the tensile strength and elongation at break of cotton/UiO-66/2St-PZS are 458.79 N and 11.04%, respectively. After 20 laundering cycles, the mechanical properties remained almost unchanged.
MoreTranslated text
Key words
Metal organic framework,Starch,Polyphosphazene,Flame retardant,Wearability
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined