High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Y. Q. Wang, J. D. Zuo, X. Xiao, K. Wu,J. Y. Zhang,G. Liu,J. Sun

CORROSION SCIENCE(2024)

引用 0|浏览14
暂无评分
摘要
In this work, the Al content -dependent microstructure evolution and oxidation behavior of co -sputtered CrAl alloyed coatings on Zr-4 alloy were systematically investigated in 1000 degrees C steam. Experimental results demonstrated that the microstructure of generated oxide scale transformed from a Cr2O3 oxide layer with embedding discrete alpha-Al2O3 particles at low Al contents to a continuous outer (alpha, theta)-Al2O3 and inner Cr2O3 bi-oxide layer at high Al contents. However, there appeared a unique eutectoid-like Cr2O3/alpha-Al2O3 multilayered oxide scale in Cr18.3Al coating, which conferred the sample with optimal oxidation resistance. The underlying oxidation mechanisms were rationalized by revealing the Al content dominated selective oxidation behavior.
更多
查看译文
关键词
CrAl alloyed coatings,Magnetron sputtering,Oxide scale,Oxidation resistance,Failure mechanisms
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要