Preparation and performance of solid thermal energy storage materials based on low-grade pyrophyllite minerals

The new sensible thermal energy storage materials were prepared by the sintering method with low-grade pyrophyllite mineral powders as main raw materials, Suzhou clay as the sintering aid and sulfite liquors as the binder. Further, the performance of sensible thermal energy storage under different size distributions and sintering temperatures was investigated and analyzed. The results show that the optimum particle size distribution is 50:15:35, the bulk density, thermal conductivity, and specific heat capacity are the largest values, which are 1.97 g cm - 3, 0.87 W m-1 K-1 and 0.63 kJ kg -1 K-1, respectively. Other properties including porosity, water absorption, flexural and compressive strength and so on are optimal under this size distribution. When the sintering temperature is 1200 degrees C, the material has a good thermal conductivity of 0.89 W m-1 K-1 and a high bulk density of 2.05 g cm -3. Meanwhile, the sample with the used temperature from 50 to 900 degrees C has the best thermal energy storage capacity of 306.29 kWh & sdot;m- 3.