Shrinkage Reduction in Nanopore-Rich Cement Paste Based on Facile Organic Modification of Montmorillonite

The organic modification of montmorillonite was successfully achieved using cetyltrimethyl ammonium bromide under facile conditions. The modified montmorillonite was subsequently used for the fabrication of montmorillonite-induced nanopore-rich cement paste (MNCP), and the shrinkage behavior and fundamental performance of MNCP were also investigated. The results indicate that alkali cations on a montmorillonite layer surface were exchanged by using CTAB under 80 degrees C, successfully achieving the organic modification of montmorillonite. As a pore-forming agent, the modified montmorillonite caused a reduction in shrinkage: the 28-day autogenous shrinkage at a design density of 400 kg/m3 and 800 kg/m3 was reduced to 2.05 mm/m and 0.24 mm/m, and the highest reduction percentages during the 28-day drying shrinkage were 68.1% and 62.2%, respectively. The enlarged interlamellar pores and hydrophobic effects caused by the organic modification of montmorillonite aided this process. Organic-modified montmorillonite had a minor influence on dry density and thermal conductivity and could contribute to an enhancement of strength in MNCP.