Effect of gamma (γ-) radiation on the opto-structural and morphological properties of green synthesized BaO nanoparticles using Moringa Oleifera leaves

In this current assessment, BaO synthesized from Moringa Oleifera leaves were irradiated using 0–75 kGy gamma radiation and investigated its physical impacts. The x-ray diffraction (XRD) data demonstrated the synthesis of tetragonal BaO, and no phase deviation was observed after irradiation. As doses are increased, the overall crystallite size were decreased due to an increase in defects and disorders. The tetragonal BaO was evident in Fourier transform infrared (FTIR) spectra prior to and following irradiation, while peak intensities and wavenumbers varied considerably. The as-prepared BaO showed a spherical shape morphology, and Field emission scanning electron microscopy (FESEM) indicated no vital deviations in it after irradiation. As irradiation shifts from 0 to 75 kGy, optical bandgap was increased from 4.55 to 4.93 eV, evaluated using Kubelka-Munk (K-M) equation from UV–vis–NIR spectrophotometer. Opto-electronic and photonic devices have challenges in extreme radiation conditions, such as space and nuclear environments. So, these assessments suggested that BaO can withstand high levels of gamma photon and could be a good option for photonic and optoelectronic instruments in an extreme gamma-ray exposed conditions.