Relevance of cold-rolling technology for the texture and anisotropy of en aw-8011a aluminum alloys

The combined effects of the reduction ratio and annealing conditions during cold rolling were investigated for the texture and anisotropy of an EN AW-8011A aluminium alloy. To characterize the microstructural and textural differences, a scanning elec-tron microscope with electron back-scattered diffraction was used. To achieve low anisotropy, the three key factors of texture were exposed: a low fraction of deformed grains according to the average grain misorientation, a large amount of random tex-ture components and the equivalent ratio between deformed and recrystallised texture components. The results of crystallo-graphic texture analysis and anisotropy values revealed that the higher ratio of total cold deformation (cold rolling reduction) and the higher ratio of cold deformation after the intermediate annealing were more favourable for the final continuous anneal-ing in terms of decreasing anisotropy. In contrast, the lower ratio of the cold deformation resulted in lower anisotropy when im-plementing batch annealing.