Unlocking Circularity Through the Chemical Recycling and Upcycling of Lignin-Derivable Polymethacrylates
MACROMOLECULES(2023)
摘要
The synthesis of polymers from lignin-derivable compounds can replace petrochemical building blocks with a renewable feedstock. However, the end-of-life management of bioderivable, nonbiodegradable polymers remains an outstanding challenge. Herein, the chemical recycling and upcycling of two higher-glass-transition temperature (>100 degrees C), lignin-derivable polymethacrylates, poly(syringyl methacrylate) (PSM) and poly(guaiacyl methacrylate) (PGM), is reported. Neat PSM and PGM were thermally depolymerized to quantitative conversions, producing their constituent monomers at high yields and purity. The deconstruction atmosphere influenced the depolymerization reaction order, and depolymerization was thermodynamically favored in air over N-2. Further, monomer bulkiness and volatility impacted depolymerization activation energies. Notably, bulk depolymerization of PSM and PGM was performed without solvent or catalyst to high polymer conversions (89-90 wt %) and monomer yields (86-90 mol %) without byproduct formation. The resultant monomers were then upcycled to narrow-dispersity polymers and phase-separated block polymers. The findings herein offer a pathway to material circularity for higher-performance, lignin-derivable polymethacrylates.
更多查看译文
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要