High-Permittivity and Bias-Voltage-Insensitive (Ba,Sr,Ca)TiO3?0.03(Bi2O3?3TiO2) Ceramics with Y5U Specification
CRYSTALS(2023)
Abstract
Class II ceramics are a material with high permittivity but low reliability of their capacitance and bias voltage due to high the temperature sensitivity of their dielectric permittivity. In this work, a BST-based (Ba0.9-xSrxCa0.1)TiO3 center dot 0.03(Bi2O3 center dot 3TiO(2)) (x = 0.2, 0.25, 0.3, 0.35, 0.4) composition with Y5U characteristics was investigated through compositional control to develop high-permittivity and voltage-stable ceramic compositions. Sr doping can increase the breakdown strength (E-b) but decreases the Curie temperature (T-c). The composition at x = 0.3 can obtain optimal comprehensive electrical properties, with high permittivity of 4206, low dielectric loss of similar to 0.009, and moderate breakdown strength (E-b) of 77.6 kV/cm, which meets Y5U specifications. Typically, a low bias-voltage dependence of capacitance is confirmed with a variation rate of 7.64% under 20 kV/cm. This strategy provides a promising candidate for high-permittivity Class II ceramic dielectrics that can be used in this field.
MoreTranslated text
Key words
lead-free ceramics,BST,dielectrics,Y5U
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined