A-site occupancy effects on structure, ionic conductivity, and thermodynamic stability of K x Mg x /2 Ti 8− x /2 O 16
MRS Advances(2024)
Abstract
K x Mg x /2 Ti 8− x /2 O 16 (1.54 ≤ x ≤ 2) hollandite samples synthesized using a conventional solid-state route were used to investigate the effect of structure, ionic conductivity, and thermodynamic stability as a function of A-site (K) occupancy. The ionic conductivity, as measured using AC impedance spectroscopy, decreased as the A-site occupancy (and K content) increased. Titanate hollandite, of the form K x Mg x /2 Ti 8− x /2 O 16 , was measured using high-temperature oxide melt solution calorimetry in sodium molybdate (3Na 2 O ∙ 4MoO 3 ) solvent at 804 ^∘ C . The enthalpies of formation are strongly exothermic indicating that they are thermodynamically stable relative to their constituent oxides. Previous studies have demonstrated increased stability with an increase in Cs content at fixed A-site occupancy. This work demonstrated an increase in the stability for the K-bearing hollandite samples with an increase in K content and tunnel occupancy. The measured enthalpies of formation (∆ H f,ox ) were in good agreement with density functional theory (DFT) predictions. Graphical abstract
MoreTranslated text
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined