Defect-curing effects of fast neutrons on n-type GaN
MATERIALS CHEMISTRY AND PHYSICS(2024)
摘要
The defect-curing effects of fast neutrons have been studied using single-crystalline GaN samples irradiated under four different neutron fluences. The conditions of each neutron irradiation were quantified by gamma-ray spectroscopy. We found that some defects generated during GaN crystal growth were cured at a low neutron fluence, and at a certain irradiation condition, the number of cured defects were larger than that of newly produced defects. Electrical parameters of Schottky barrier diodes fabricated by using samples from every batch demonstrated different levels of defect-curing effects. In terms of optical characteristics, the defect-curing effects were checked by photoluminescence spectroscopy measurements. Through synchrotron X-ray topography characterization, the number of cured, newly generated, and altered defects were quantified and directly confirmed the curing effects of fast neutrons.
更多查看译文
关键词
GaN,Defect curing,Neutron transmutation effect,Synchrotron monochromatic beam X-ray,topography (SMBXT)
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要