Anisotropic behavior of as-extruded 7003 aluminum alloy under quasi-static compression and high-speed impact
INTERNATIONAL JOURNAL OF IMPACT ENGINEERING(2024)
摘要
The anisotropic behavior of as-extruded 7003 aluminum alloy under quasi-static compression and high-speed impact was studied using samples with axes parallel to extrusion direction (ED) (0 degrees sample), at an angle of 45 degrees to ED (45 degrees sample), and perpendicular to ED (90 degrees sample). The experimental results show that the yield stress of the 0 degrees sample is the highest, while the 45 degrees sample is the lowest. Compared with other samples, the 90 degrees sample is more sensitive to the applied strain rate, which experiences a rapid failure after reaching peak stress under high-speed impact. Under quasi-static compression and high-speed impact, the 0 degrees sample exhibits nearly uniform deformation, while the 45 degrees and 90 degrees samples exhibit anisotropy behavior. Due to the occurrence of adiabatic shear, the plastic deformation anisotropy in 45 degrees and 90 degrees samples under high-speed impact is more significant compared to quasi-static compression. For the 45 degrees and 90 degrees samples, the r values, which characterize plastic deformation anisotropy, decrease from 0.77 to 0.82 under quasi-static compression to 0.46 and 0.40 under high-speed impact. In addition, adiabatic shear bands are observed in all deformed samples under highspeed impact, while only the 90 degrees sample fractures. Due to the significant difference in Schmidt factors along ED and transverse direction (TD), plastic deformation of the 90 degrees sample under high-speed impact is mainly concentrated in TD, while the deformation in ED is very small. The extremely uneven deformation leads to earlier nucleation and faster development of ASBs in TD, causing the 90 degrees sample to fracture under high-speed impact.
更多查看译文
关键词
As-extruded 7003 aluminum alloy,Anisotropy,Microstructure,Failure
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要