Elastoplastic Fracture Mechanics Approach to the Crack Growth Rate Computation of Modified Pipe Steels
Strength of Materials(2023)
摘要
A mechanophysical model for crack growth kinetics computation on stress corrosion fracture of modified 06G2BA and 08KhMCHA pipe steels is adequately expressed through the plane stress-strain state dα/dt and dJ/dt ratios that are dependent on the strain crack tip rate. The crack growth accelerated by an aggressive environment occurs under static and cyclic loading due to transient dissolution and repassivation processes at the crack tip. Such accelerations are divided into three categories, determined by the strain rate: mechanical cracking (fatigue crack and stationary plastic crack), corrosion-accelerated mechanical cracking (corrosion fatigue and corrosion-accelerated plastic crack), and sulfide stress corrosion fracture. Metallographic studies revealed the change in the crack nucleation and propagation mechanisms, from transcrystalline to intercrystalline, related to the viscoplastic and brittle structure of steel specimens cyclically loaded and simultaneously affected by a corrosive environment.
更多查看译文
关键词
pipe,strain,fracture,crack resistance,cracks,pores,nonmetallic inclusions
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要