High-performance and functional fully bio-based polylactic acid/ polypropylene carbonate blends by in situ multistep reaction-induced interfacial control

Using a solvent-free radical grafting technique, glycidyl methacrylate (GMA) and maleic anhydride (MAH) were used as functionalized graft monomers, styrene (St) as a copolymer monomer, and grafted onto polylactic acid (PLA). A series of PLA-g-(GMA/MAH-co-St) graft copolymers were prepared by adjusting the GMA/MAH ratio. Subsequently, the prepared graft copolymers were used as a compatibilizer with PLA and polypropylene carbonate (PPC) for melt blending to prepare PLA/PPC/PLA-g-(GMA/MAH-co-St) blends. The effects of changes in the GMA/MAH ratio in the graft copolymer on the thermodynamics, rheology, optics, degradation performance, mechanical properties, and microstructure of the blend were studied. The results found that GMA, MAH, and St were successfully grafted onto PLA, and the PLA-g-(GMA/MAH-co-St) graft copolymer obtained from the reaction had a good toughening effect on the PLA/PPC blend system, which significantly improved the mechanical properties of the PLA/PPC/PLA-g-(GMA/MAH-co-St) blend without reducing its degradation performance, resulting in a biodegradable blend material with excellent comprehensive performance. In the PLA-g-(GMA/ MAH-co-St) grafting reaction system, when GMA/MAH = 1.5/1.5 (w/w), the grafting degree of the graft copolymer increased most significantly, from 0.83 phr to 1.51 phr. This composition of graft copolymer can effectively improve the compatibility between PLA and PPC. The resulting PLA/PPC blend can maintain good melt flow properties (MFR of 14.51 g/10 min), high transparency, and low haze (light transmittance of 91.56 %, haze of 20.5 %), while significantly improving its thermal stability (T95%, Tmax, and Et increased by 12.87 degrees C, 20.33 degrees C, and 32.00 kJ/mol, respectively). Moreover, when introducing PLA-g-(GMA/MAH-co-St) (GMA/MAH = 1.5/1.5 (wt/wt)) graft copolymer into the system, the toughness of the PLA/PPC/PLA-g-(GMA/MAH-co-St) blend system is optimal, with the notch impact strength and fracture elongation increasing to 184.6 % and 535.4 % of the PLA/PPC blend, respectively, at which point the fracture surface of the impact sample shows a wrinkled fracture feature indicative of toughness.