Polyethylene bearing wear of the oxford unicompartmental knee arthroplasty: ten-year results of a randomized controlled trial comparing cemented and cementless fixation

Abstract Introduction The Oxford Unicompartmental Knee Replacement's (OUKR's) fully-congruent design minimises polyethylene wear. Consequently, wear is a rare failure mechanism. Phase-3 OUKR linear wear at 5 years was higher than previous OUKR phases, but very low compared to fixed-bearing UKRs. This study aimed to measure OUKR bearing wear at 10 years and investigate factors that may affect wear. Methodology Bearing thickness for 39 OUKRs from a randomised study was calculated using radiostereometric analysis at regular intervals up to 10 years. Data for 39 and 29 OUKRs was available at 5 and 10 years, respectively. As creep occurs early, wear rate was calculated using linear regression between 6 months and 10 years. Relationships between wear and patient factors, fixation method, Oxford Knee Score (OKS), bearing position, and component position were analysed. Results The mean wear rate was 0.06mm/year. Fixation method, age, OKS, component size, and bearing size had no correlation with wear. A higher BMI was associated with lower wear (p=0.01). Bearings more than 4mm from the wall had significantly more wear (p=0.04) than those less than 4mm from the wall. There was a linear correlation between the femoral component contact area on the bearing and wear (p=0.04). Conclusions Phase-3 bearing wear rate is constant, significantly higher than previous OUKR phases at 10 years, and may increase the risk of long-term bearing failure. To minimise complications associated with wear, size 4 bearings should be used in young patients and manufacturing bearings from more durable, highly crosslinked polyethylene should be studied.