Stacking Order Induced Anion Redox Regulation for Layer‐Structured Na_0.75Li_0.2Mn_0.7Cu_0.1O₂ Cathode Materials

Stacking order plays a key role in defining the electrochemical behavior and structural stability of layer-structured cathode materials. However, the detailed effects of stacking order on anionic redox in layer-structured cathode materials have not been investigated specifically and are still unrevealed. Herein, two layered cathodes with the same chemical formula but different stacking orders: P2-Na0.75 Li0.2 Mn0.7 Cu0.1 O2 (P2-LMC) and P3-Na0.75 Li0.2 Mn0.7 Cu0.1 O2 (P3-LMC) are compared. It is found that P3 stacking order is beneficial to improve the oxygen redox reversibility compared with P2 stacking order. By using synchrotron hard and soft X-ray absorption spectroscopies, three redox couples of Cu2+ /Cu3+ , Mn3.5+ /Mn4+ , and O2- /O- are revealed to contribute charge compensation in P3 structure simultaneously, and two redox couples of Cu2+ /Cu3+ and O2- /O- are more reversible than those in P2-LMC due to the higher electronic densities in Cu 3d and O 2p orbitals in P3-LMC. In situ X-ray diffraction reveals that P3-LMC exhibits higher structural reversibility during charge and discharge than P2-LMC, even at 5C rate. As a result, P3-LMC delivers a high reversible capacity of 190.3 mAh g-1 and capacity retention of 125.7 mAh g-1 over 100 cycles. These findings provide new insight into oxygen-redox-involved layered cathode materials for SIBs.