Intumescent fireproof coatings based on zeolite‐like cement matrices

ce/papers(2023)

引用 0|浏览8
暂无评分
摘要
Abstract Concrete and reinforced concrete building structures (for example, such as tunnels) lose carrying ability in case of high‐temperature fire action. The aim of the research is to study the prevention of reinforced concrete structures (for example, such as tunnels) under fire action in case of using the proposed coating based on the alkaline aluminosilicate binder, which would not consist of organic components dangerous to health. The ratios between constituent oxides in the binder which ensure the ability to bloat the coating under fire action were determined. The performance properties of developed fire protective coating were defined after artificial aging (cycles of alternate drying and cooling) and fire action: bloating factor ‐ 2.0…5.1, adhesion strength ‐ 6.6…8.0 MPa, compressive strength ‐ 2.3…4.5 MPa, cohesive strength of 1.2…1.5 MPa, thermal conductivity coefficient ‐ 0.042…0.066 W/m‐°C, total porosity ‐ 92…97 %. The temperature at which the coating starts to bloat = 200…250 °C has been developed. The results of the test held in the open air suggested drawing a conclusion that with a coating thickness of 6 mm protection of the reinforced concrete from fragile fracture and from plastic deformations in the metal of the reinforcement they provided under fire exposure for a period of 3 hours.
更多
查看译文
关键词
zeolite‐like,cement
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要