Experimental and numerical techniques to evaluate coal/biomass fly ash blend characteristics and potentials

Fossil and renewable fuels are used by industrial units that produce energy-intensive products. Competitive fuel pricing encourages these fuel sources' usage globally, particularly in developing nations, which leads to large volumes of byproducts like fly ash among thermal power plant operators. The elements and compounds found in coal fly ash (CFA) and biomass fly ash (BFA) can be utilized through several engineering applications. This study aims to assess typical CFA and BFA samples quantitatively and qualitatively via techniques such as ultimate analysis (CH-S), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray fluorescence (XRF) elemental analysis, and ash fusion temperature (AFT), to anticipate the ideal ratios of coal to biomass blends for combustion applications while adhering to environmental regulations. The optimal blend, consisting of 75 % CFA and 25 % BFA, exhibited improved carbon (C%) and hydrogen (H%) percentages, increasing from 2.5 % to 4.67 % and from 0 % to 0.12 %, respectively. These improvements were further confirmed by the observed functional groups in FTIR, indicating a rising trend in both carbon and hydroxyl groups from BFA to CFA. XRF and XRD also confirmed it and TGA also showed optimum mass loss (ML%) behavior of 14.55 % for 75CFA + 25BFA. According to slagging and fouling indices, the values of R-B/A, R-s, and F-u indicate a reduction in slagging and fouling issues through the blending of CFA with BFA. Simultaneously, the fusion temperature increased from 1181 degrees C to 1207 degrees C. CFA was found to increase the AFT of the BFA from 1197 degrees C to 1247 degrees C, mitigating their propensity. This suggests that a blend of 75CFA + 25BFA results in lower to medium range of slagging and fouling. However, AFI and BAI indicate a slightly higher range. AFT analysis further validates the conclusions drawn from the indices. The ternary phase diagram shows that the ash's melting point increases in the optimum blend. This is attributed to a reduced content of K2O (<15 %) and increased proportions of >50 % CaO and SiO2, effectively inhibiting slagging, agglomeration, and deposition. Meanwhile, the blend maintains a medium level of acidity and susceptively to corrosion, as observed in the case of 75CFA + 25BFA. The identification of optimal blend ratios can be anticipated to offer essential solutions for future research, aiming to ensure smooth industrial operations and regulatory compliance in power plants.