High-Performance Full Sodium Cells Based on MgO-Treated P2-Type Na_0.67(Mn_0.5Fe_0.5)_1-xCo _xO₂ Cathodes

Herein, we design a cathode material based on layered Na-2/3(Mn1/2Fe1/2)O-2 for practical application by combining the Co substitution and MgO treatment strategies. The oxides are prepared via solid-state reactions at 900 degrees C. The structure, morphology, and oxidation state of transition metal ions for Co-substituted and MgO-treated oxides are carefully examined via X-ray diffraction, IR and Raman spectroscopies, FESEM with EDX, specific surface area measurement, and XPS spectroscopy. The ability of oxides to store sodium reversibly is analyzed within a temperature range of 10 to 50 degrees C via CV experiments, galvanostatic measurements, and EIS, using half and full sodium ion cells. The changes in the local structure and oxidation state of transition metal ions during Na+ intercalation are monitored via operando XAS experiments. It is found that the Co substituents have a positive impact on the rate capability of layered oxides, while Mg additives lead to a strong increase in the capacity and an enhancement of the cycling stability. Thus, the highest capacity is obtained for 2 at.%-MgO-treated Na-2/3(Mn1/2Fe1/2)(0.9)Co0.1O2 (175 mAh/g, with a capacity fade of 28% after 100 cycles). In comparison with Co substituents, the Mg treatment has a crucial role in the improvement of the lattice stability during the cycling process. The best electrode materials, with a chemical formula of 2 at.%-MgO treated Na-2/3(Mn1/2Fe1/2)(0.9)Co0.1O2, were also used for the full cells design, with hard carbon as an anode. In the voltage window of 2-4 V, the capacity of the cells was obtained as 78 mAh/g and 51 mAh/g for applied current densities of 12 mA/g and 60 mA/g, respectively.