Molecular beam epitaxy growth of superconducting tantalum germanide

Developing alternative material platforms for use in superconductor-semiconductor hybrid structures is desirable due to limitations caused by intrinsic microwave losses present in commonly used III/V material systems. With the recent reports on tantalum superconducting qubits that show improvements over the Nb and Al counterparts, exploring Ta the superconductor in hybrid material systems is promising. Here, we study the growth of Ta on semiconducting Ge (001) substrates grown via molecular beam epitaxy. We show that at a growth temperature of 400 degrees C, the Ta diffuses into the Ge matrix in a self-limiting nature resulting in smooth and abrupt surfaces and interfaces with roughness on the order of 3-7 & Aring; as measured by atomic force microscopy and x-ray reflectivity. The films are found to be a mixture of Ta5Ge3 and TaGe2 binary alloys and form a native oxide that seems to form a sharp interface with the underlying film. These films are superconducting with a T-C similar to 1.8-2 K and H-C(perpendicular to)similar to 1.88 T, H-C(parallel to)similar to 5.1 T. These results show this tantalum germanide film to be promising for future superconducting quantum information platforms