Evaluation of mechanical, optical, and fluoride-releasing properties of a translucent bulk fill glass hybrid restorative dental material

Objective: Measure and compare the mechanical properties, translucency, and fluoride-releasing capabilities of EQUIA Forte HT against Fuji IX GP and ChemFil Rock.Materials and methods: Ten specimens of each material were fabricated for compressive strength (CS), flexural strength (FS), and surface hardness analysis at 24 h and 7 days. The L*a*b* values were measured against a black-and-white background using a spectrophotometer to analyze the translucency parameter (TP). Fluoride release was recorded after 2 months of immersion in distilled water. The mean data was analyzed by 1- and 2-way ANOVA (alpha = 0.5).Results: EQUIA Forte HT showed higher CS, surface hardness, and FS values (p < 0.05) compared with Fuji IX GIC, while no significant difference was found in FS values between EQUIA Forte HT and Chemfil Rock (p > 0.05). The EQUIA Forte HT exhibited significantly higher translucency in comparison to both ChemFil Rock (p < 0.001) and Fuji IX GICs (p < 0.05). An increase (p > 0.05) of fluoride release was observed for EQUIA Forte HT.Conclusion: The EQUIA Forte HT Glass-ionomer cements (GIC) offers enhanced translucency, improved strength, and enhanced fluoride-releasing properties compared to the traditionally used Fuji IX GIC and ChemFil Rock GICs. This material might have a wide range of clinical applications due to its improved strength and optical properties.