Mechanical and fractographic assessment of different types of endodontic post systems used in the restoration of devitalized teeth
ROMANIAN JOURNAL OF ORAL REHABILITATION(2023)
摘要
Aim of the study The resistance to functional and parafunctional stresses of devitalized teeth is multifactorial, but the choice of a specific endodontic post system influences the restoration's longevity. This primary ex-vivo study aims to evaluate the compressive strength of three different non-metallic post systems and to analyze the appearance of fracture surfaces (fractography) using optical microscopy and alongside statistical analysis that validates their behavior.Material and methods For this study, three groups of non-metallic post systems were considered as follows: glass fiber-reinforced photopolymerized resin, pressed ceramic, and pressed ceramic on glass fiber. The sample size has a length of 0.8mm and an average diameter of 0.2mm. Subsequently, the samples were embedded in self-polymerizing resin to be secured in the workspace of the Zwick Roell 5kN testing machine that works at loading speed of 2 mm/min. The fractographic analysis of the obtained surfaces were performed with the Optika SLX3 microscope and C-B16 camera, at magnifications of 20, 50, and 90X.Results The data obtained from the mechanical tests were statistically processed and the results showed significant differences regarding the compressive strength of non-metallic post systems made from different materials and different technologies. Conclusions The group containing posts made from pressed ceramic on glass fiber exhibited higher resistance to applied compressive forces.
更多查看译文
关键词
glass fiber reconstitution,pressed ceramic,compressive strength,fractography
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要