Effect of irradiation damage defects on the impurity containing molten salt corrosion behavior in GH3535 alloy
CORROSION SCIENCE(2023)
摘要
This study explores the corrosion response of irradiated nickel-based GH3535 alloy in impurity-enriched molten FLiNaK salt at 650 degrees C. Displacement damage resulting from Au ion irradiation formats dislocation loops, whose distribution is influenced by subsequent He ion irradiation and He bubble formation. Samples irradiated with Au ions exhibit a shallow corrosion layer with big-size and dense distributed Cr2O3 particles, while a contrasting trend is observed in samples irradiated with He ions. Displacement damage decelerates Cr outward diffusion by promoting protective Cr2O3 formation with SO42-impurities, thereby inhibiting impurity-accelerated corrosion. However, the accelerating effect of He bubbles subsequently counteracts this inhibitory impact on corrosion.
更多查看译文
关键词
Nickel based alloy,Molten salt corrosion,Displacement damage,He bubbles,Impurity
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要