Composite Powders Synthesized from the Water Solutions of Sodium Silicate and Different Calcium Salts (Nitrate, Chloride, and Acetate)

Composite powders were synthesized from the water solutions of sodium silicate and different calcium salts (nitrate, chloride, and acetate) at a Ca/Si molar ratio of 1.0. According to the XRD data, all the synthesized powders included hydrated calcium silicate Ca1,5SiO3,5 center dot xH2O (Ca/Si molar ratio = 1.5) and calcium carbonate CaCO3 (Ca/Si molar ratio = infinity). The presence of H2SiO3 or SiO2 center dot xH2O in the synthesized powders was assumed to be due to the difference between the Ca/Si molar ratio of 1.0 specified by the synthesis protocol and the molar ratio of the detected products. Reaction by-products (sodium nitrate NaNO3, sodium chloride NaCl, and sodium acetate NaCH3COO) were also found in the synthesized powders after filtration and drying. According to the XRD data phase composition of all powders after washing four times consisted of the quasi-amorphous phase and calcium carbonate in the form of calcite. Calcium carbonate in the form of aragonite was detected in powders synthesized from calcium chloride CaCl2 and calcium nitrate Ca(NO3)2 before and after washing. Synthesized powders containing reaction by-products and washed powders were used for the preparation of ceramics at 900, 1000, and 1100 degrees C. The phase composition of the ceramic samples prepared from the washed powders and powder containing NaCl after firing at 900 and 1000 degrees C consisted of beta-wollastonite beta-CaSiO3, and, after firing at 1100 degrees C, consisted of both beta-wollastonite beta-CaSiO3 and pseudo-wollastonite alpha-CaSiO3. The phase composition of the ceramic samples prepared from powders containing sodium nitrate NaNO3 and sodium acetate NaCH3COO after firing at 900, 1000, and 1100 degrees C consisted of calcium sodium silicates, i.e., Na2Ca2Si3O9 (combeite) and Na2Ca3Si2O8. Synthesized and washed composite powders can be used for the preparation of biocompatible materials, in the technology of construction materials, and as components of lunar soil simulants.