Techno-functional characterization of gelatin extracted from the smooth-hound shark skins: Impact of pretreatments and drying methods

Gelatin derived from marine by-products could be an interesting alternative to classic mammalian gelatin. The pretreatment and extraction conditions could influence the size of the resulting peptide chains and therefore their techno-functional properties. Thus, it is important to optimize the production process to get a gelatin for the appropriate applications. Skin pretreatment was done by microwaves or oven-drying and the extracted gelatin was dried by spray-or freezedrying. Freeze-dried gelatin extracted from untreated skin (FGUS) had the highest gelatin yield (10.40%). Gelatin proximate composition showed that proteins were the major component (87.12-89.95%), while lipids showed the lowest contents (0.65-2.26%). Glycine showed the highest level (299-316/1000 residues) in the extracted gelatins. Proline and hydroxyproline residues of gelatins from untreated skin were significantly higher than those from pretreated skin gelatin. FTIR spectra were characterized by peaks of the amide A (3430-3284 cm -1), B (30002931 cm -1), I (1636-1672 cm -1), II (1539-1586 cm -1) and III (1000-1107 cm -1). Spray-drying decreased the gelling properties of gelatins, since it reduced gelling and melting temperatures compared to freeze-drying. Skin pretreatment significantly reduced the gel strength of gelatin by about 50-100 g depending on the gelatin drying method. The FGUS showed better surface properties compared to other gelatins. The highest emulsion activity index (39.42 & PLUSMN; 1.02 m2/g) and foaming expansion (172.33 & PLUSMN; 2.35%) were measured at 3% FGUS. Therefore, the promising properties of freeze-dried gelatin derived from untreated skin, gave it the opportunity to be successfully used as a techno-functional ingredient in many formulations.