Biomodification of eroded and abraded dentin with epigallocatechin-3-gallate (EGCG).

This study aimed to evaluate in vitro the effects of epigallocatechin-3-gallate (EGCG) as a biomodifier of eroded and abraded dentin. Forty dentin specimens were obtained from the buccal surface of bovine teeth. The specimens were randomly distributed in 4 groups according to dentin substrate: sound or eroded/abraded and dentin biomodification: with 0.5% EGCG and no biomodification (control group). Specimens were subdivided according to aging time: 24 h and 3 months for the analysis of microtensile bond strength (n = 10), morphology of the adhesive interface by SEM (n = 3) and dentin micropermeability by fluorescence microscope (n = 8). Statistical analysis was performed using SPSS system version 20.0 with a significance level of 5%. The results revealed that the control group with eroded-abraded dentin exhibited the lowest bond strength values at 24 h and 3 months. However, the application of 0.5% EGCG as a biomodifier significantly increased bond strength on both sound and eroded-abraded substrates. After 3 months, all groups exhibited an adhesive interface with a more intense fluorescence in the adhesive layer, indicating an increase in porosity at the interface. In conclusion, the EGCG application as a biomodifier enhanced bond strength on both sound and eroded-abraded dentin substrates, however, adhesive interfaces are more regular when restorations are performed on sound dentin, regardless of the biomodification with EGCG.