Enhanced cavitation erosion resistance of GX40CrNiSi25-20 cast stainless steels by surface TIG re-melting

This study aimed to reduce cavitation erosion effects by improving the surface properties of high-alloyed steel cast parts using the tungsten inert gas (TIG) surface physical modification technique. Local surface melting was performed at different linear energies (El = 4080–8880 J/cm) by varying the current between 100 and 200 A at a constant voltage of 10.2–11.1 V. Hardness increased from 210 to 390 HV5 when a TIG current of 150 A with a linear energy of El = 6630 J/cm was implemented.