Features of Metalorganic Chemical Vapor Deposition Selective Area Epitaxy of AlzGa1−zAs (0 ≤ z ≤ 0.3) Layers in Arrays of Ultrawide Windows

V. V. Shamakhov, С. О. Сліпченко, D. N. Nikolaev,І. П. Сошніков, А. Н. Смирнов, I. A. Eliseyev, A. M. Grishin,Matvei Kondratov, A. E. Rizaev,N. A. Pikhtin, P. S. Kop’ev

Technologies (Basel)(2023)

引用 0|浏览2
暂无评分
摘要
AlzGa1−zAs layers of various compositions were grown using metalorganic chemical vapor deposition on a GaAs substrate with a pattern of alternating SiO2 mask/window stripes, each 100 µm wide. Microphotoluminescence maps and thickness profiles of AlzGa1−zAs layers that demonstrated the distribution of the growth rate and z in the window were experimentally studied. It was shown that the layer growth rate and the AlAs mole fraction increased continuously from the center to the edge of the window. It was experimentally shown that for a fixed growth time of 10 min, as z increased from 0 to 0.3, the layer thickness difference between the center of the window and the edge increased from 700 Å to 1100 Å, and the maximum change in z between the center of the window and the edge reached Δz 0.016, respectively. Within the framework of the vapor -phase diffusion model, simulations of the spatial distribution of the layer thickness and z across the window were carried out. It was shown that the simulation results were in good agreement with the experimental results for the effective diffusion length D/k: Ga—85 µm, Al—50 µm.
更多
查看译文
关键词
chemical vapor deposition,ultrawide windows
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要