Enhanced Electrocatalytic Oxidation of Sterols using the Synergistic Effect of NiFe-MOF and Aminoxyl Radicals

Conventional oxidation methods of sterol intermediates using the heavy metal chromium as an oxidant has critical drawbacks, such as high toxicity and environmental pollution. Electrocatalytic oxidation (ECO), on the other hand, is considered a promising alternative to conventional processes owing to its high efficiency, eco-friendliness, and controllability. However, ECO currently faces two major challenges: low current densities and reduced space-time yields. In this study, a single-step solvothermal method was employed to synthesize self -supported nickel -iron metal -organic framework (NiFeMOF) nanosheet electrocatalysts on graphite felt. Various analytical techniques were employed to comprehensively characterize the synthesized NiFe-MOF, including scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, and Brunauer-Emmett-Teller (BET) analysis Furthermore, we implemented a synergistic electrocatalytic strategy by combining the NiFe-MOF catalyst with aminoxyl radicals, i.e., 4acetamido-2,2,6,6-tetramethyl-1-piperidine-N-oxyl (ACT), to enhance the performance of the ECO reaction. According to the results of structural characterization, the synthesized NiFe-MOF exhibited an amorphous nanosheet structure with a high specific surface area and microporosity. Moreover, we successfully achieved continuous flow with enhanced mass transfer during the electrocatalytic oxidation of 19-hydroxy-4-androstene-3,17-dione (1a) at a current density of 100 mA center dot cm-2. The optimal reaction conditions for the ECO reaction were as follows: 100 mmol center dot L-1 concentration of 1a, 10% (molar fraction) of ACT, a 1 mol center dot L-1 Na2CO3/acetonitrile electrolyte (6 : 4), room temperature, pH 12.5, and a flow rate of 225 mL center dot min-1. Under these conditions, the conversion and selectivity of the reaction reached outstanding levels of 99 and 98%, respectively. Moreover, the space-time yield was calculated to be as high as 15.88 kg center dot m-3 center dot h-1, with a remarkable 35fold increase compared to that achieved in a batch reactor. The NiFe-MOF/ACT synergistic system demonstrated a high conversion rate for ECO even after 10 reaction cycles. To assess the system's efficacy in converting other sterols, we conducted an analysis of substrate expansion, which yielded conversion rates exceeding 95%. The SEM, TEM, and XPS results of the catalyst obtained before and after the reaction indicated that the alkaline electrolyte could effectively reconstitute the NiFe-MOF structure, leading to a significant improvement in its performance. By leveraging a ten -fold increased surface area of the NiFe-MOF and constructing a continuous flow electroreactor for ECO with a constant current, we achieved a remarkable space-time yield of 12.99 kg center dot m-3 center dot h-1. Thus, we developed a synergistic electrocatalytic oxidation strategy based on NiFe-MOF/ACT, and this study not only provides valuable insights for realizing the selective oxidation of sterols but also contributes to the advancement of sustainable and efficient chemical processes.