Thermoelectric properties of sintered polycrystalline ZnIn 2 S 4
Journal of Materials Research(2011)
摘要
Ceramic compacts of spinel-type ZnIn 2 S 4 and IIIa-ZnIn 2 S 4 polytype with a layer structure were synthesized by the reaction-sintering of mixed powders of ZnS and In 2 S 3 at 723 K and 1073 K in Ar (containing 1° H 2 ) atmosphere, respectively. The thermoelectric properties were investigated in the temperature range from 473 to 873 K. Thermoelectric figure of merit of the IIIa type was much larger than that of the spinel type, and it was slightly higher than the figure of merit of (ZnO) 9 In 2 O 3 , which is known to show the largest value among the oxide homologous compounds. To improve the thermoelectric properties, a c -plane-oriented sintered body of the IIIa polytype was successfully fabricated by a usual ceramic process. The figure of merit in the direction on the c plane was larger than on the ab plane due to higher electrical conductivity on the c plane and increased with increasing temperature showing the largest value of 1.3 × 10 −4 K −1 at 873 K.
更多查看译文
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要