Hydrangea-like NiO@KNbO3 As Catalyst Doping for MgH2: Boosting Hydrogen Storage Performance
Journal of alloys and compounds(2023)
Abstract
MgH2 is regarded as one of the most favorable materials for hydrogen storage caused by its safety, high efficiency, considerable capacity for storing hydrogen, and low cost. However, the application of this ma-terial is limited owing to subpar thermodynamics and kinetics, which can be improved via combination with other materials. A hydrangea-like NiO@KNbO3 was prepared by solvent thermal, hydrothermal, and calcination methods. Then, different amounts of NiO@KNbO3 (3, 5, 7, and 10 wt %) were added to MgH2 using ball-milling. MgH2 composite material doped with 5 wt % NiO@KNbO3 exhibits the most superior hydrogen storage performance, with a hydrogen absorption capacity of 4.95 wt % H2 within 5 min at 150 celcius and 1.5 MPa H2 pressure. Furthermore, H2 release started approximately at 175 & DEG;C with 5.96 wt % H2 at 300 & DEG;C. The composite's H2 desorption activation energy was decreased to 71.75 kJ/mol. The Mg2NiH4/ Mg2Ni generated in situ can serve as a "hydrogen pump" by creating numerous activation sites and path-ways for hydrogen diffusion, thereby facilitating H2 dissociation during the process of hydrogen absorption. Additionally, the NiO@KNbO3-doped MgH2 samples exhibited excellent integrated hydrogen storage properties due to the combined effect of KNbO3 and the in situ formed NbO. The study provides clear evidence that NiO@KNbO3, a bimetallic oxide, can effectively enhance the hydrogen storage performance of MgH2 as an additive. Furthermore, the straightforward synthesis of NiO@KNbO3 offers guidance for the development of high-performance oxide catalysts that can improve the properties of MgH2.& COPY; 2023 Elsevier B.V. All rights reserved.
MoreTranslated text
Key words
Hydrangea-likeNiO@KNbO3,Hydrogen storage properties,Magnesium hydride,Renewable energy
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined