Influence of NaCl on Magnetic Properties of MgFe 2 O 4 Nanoparticles Synthesized by Gel Combustion
International Journal of Self-Propagating High-Temperature Synthesis(2023)
摘要
The effect of sodium chloride (NaCl) on the magnetism of nanopowders of the spinel ferrite (MgFe 2 O 4 ) produced using a salt-assisted solution combustion synthesis was investigated. X-ray diffraction (XRD) analysis was conducted to evaluate crystalline structure and phase composition of the synthesized materials. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) was used to evaluate the particle size and morphology. Magnetic behavior was analyzed by measuring and analyzing the respective hysteresis loops using a vibrating sample magnetometer (VSM). The characterization showed that the presence of NaCl affects the phase composition, size, and dispersion of the nanoparticles, as well as their magnetic behavior. The theoretical size of the nanoparticles was calculated using the Scherrer equation, obtaining sizes of about 21.07 nm for the nanoparticles without salt, 5.90 nm for the sample salt content of 1.7 mol and 6.48 nm—for 3.4 mol. The synthesized nanoparticles showed a drastic decrease in coercivity field, remanence, and saturation with increasing salt content. Therefore, the salt content is a crucial parameter in controlling the morphology and magnetic properties of the nanoparticles obtained by the solution combustion route.
更多查看译文
关键词
gel combustion, magnesium ferrite, superparamagnetism, nanoparticles, spinel
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要