Bamboo-like N-doped carbon tubes encapsulated Co2P–Fe2P derived from zeolitic imidazolate framework as an efficient trifunctional electrocatalyst for water splitting and Zn-air batteries

The development of high-performance and stable trifunctional electrocatalysts is a pressing challenge for the practical application of water splitting and regenerative Zn-air batteries. Herein, bamboo-like N-doped carbon tubes encapsulated Co2P–Fe2P nanoparticles (CoFe-PN/C) was fabricated via a facile template-sacrificial approach by using CoZn-ZIF trapping Fe3+ (CoFeZn/C) as the precursor. The incorporation of Fe3+ was achieved by the one-pot synthesis approach during crystallization of ZIF, which led to the generation of the unique bamboo-like tube structure under the condition of simultaneous phosphating and carbonization. Benefiting from the large surface area, the optimized electronic structure of active sites and the unique bamboo-like nanotube, the resultant CoFe-PN/C can be used as the trifunctional electrocatalyst possessing a small overpotential at 10 mA cm−2 for the HER (178 mV) and OER (300 mV), as well as a high half-wave potential of 0.884 V for ORR (40 mV more positive than that of commercial 20 wt% Pt/C). Moreover, the self-designed CoFe-PN/C||CoFe-PN/C alkaline electrolyzer driving 50 mA cm−2 only need operating potential of 1.84 V and the maximum discharge power density of the CoFe-PN/C-assembled ZABs could achieve 152.0 mW cm−2, superior to those of Pt/RuO2 couple. This work will facilitate the development and application of trifunctional electrocatalysts based on bi-transition metallic phosphides for energy conversion and storage technology.