Composite resin reinforced with silk nanoparticles from Bombyx mori cocoon for dental applications.

Brazilian dental journal(2023)

引用 0|浏览4
暂无评分
摘要
The objective of this work was to evaluate the mechanical performance of Z350 resin composite modified with Bombyx mori cocoons silk nanoparticles for dental applications. Four experimental groups were analyzed G0% = Filtek Z350 resin composite (control); G1% = Filtek Z350 with 1% of silk nanoparticles; G3% = Filtek Z350 with 3% of silk nanoparticles; G5% = Filtek Z350 with 5% of silk nanoparticles. It was employed scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, 3-point flexural strength test, Knoop hardness test, and surface roughness. From 3-point flexural strength tests the control group presented the best results G0% = 113.33 MPa (±23.73). The higher flexural modulus was shown by groups G3% = 29.150 GPa (±5.191) and G5% = 34.101 GPa (±7.940), which are statistically similar. The Knoop microhardness test has shown statistical difference only among the G3% group between the top 80.78 (± 3.00) and bottom 68.80 (±3.62) and no difference between the groups. The roughness test presented no statistical difference between the groups. The incorporation of silk nanoparticles reduced the flexural strength of Z350 resin composite. The surface roughness and microhardness tests showed no changes in any of the groups studied.
更多
查看译文
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要